Technical ceramics · Zibo, Shandong
Technical ceramics in alumina, zirconia and SiC, ground to your drawing.
Pressed, sintered and diamond-ground in our own plant.
See the six materialsMaterials
Six materials
Typical values, not guarantees. Each grade sheet lists the test method.
KW-A995 · Alumina 99.5%
- 3.90 g/cm³
- HV 1,700
KW-A95 · Alumina 95%
- 3.65 g/cm³
- HV 1,400
KW-ZY · Zirconia Y-TZP
- 6.05 g/cm³
- 1,000 MPa
KW-ZTA · Zirconia toughened alumina
- 4.15 g/cm³
- 650 MPa
KW-SS · Sintered silicon carbide
- 3.10 g/cm³
- HV 2,500
KW-RB · Reaction-bonded silicon carbide
- 3.02 g/cm³
- beams to 2,500 mm
Parts
Typical parts
Every part is cut to the drawing you send.
- 01
Seal rings and bushings
KW-SSØ20–400 mm
Pumps and mixers in chemical duty
- 02
Wear liners and nozzles
KW-A95 · KW-RBTiles to 300 × 300 mm
Slurry pumps and cyclones
- 03
Plungers, pins and guides
KW-ZYØ2–60 mm
Dosing pumps and filling lines
- 04
Kiln beams and rollers
KW-RBBeams to 2,500 mm
Tile, porcelain and battery-material kilns
Capability
Limits we hold
Typical production values on finished parts; limits for your part are quoted per drawing.
Ground bore and OD
±0.005 mm
CNC diamond grinding
Lapped seal faces
Ra 0.05 µm
Flat to 2 helium light bands
Longest RBSiC beam
2,500 mm
Kiln furniture, one piece
SSiC sintering
2,100 °C
Pressureless, argon atmosphere
Factory
Powder to part
Every lot ships with a density, hardness and dimension report.
2009
Plant founded
38,000 m²
Floor area
32
CNC diamond grinders
Tested to
- ISO 9001:2015
- ISO 14001:2015
- ASTM C1161
- ASTM C1327
- EN 843-1
- REACH / RoHS
Quote
Send your drawing
- sales@kilnwick.example.com
- Reply within one working day, with a manufacturability review.